Bimetallic Twin Screw & Barrel

 

Wc-10 tungsten carbide alloy , with the characteristic of high hardness ,high hard-wearing, corrosion resistance , and high- temperature resistance ,the hardness of alloy layer reaches HRC60-65, thus having the service life of two or three times longer than the nitrided barrel. It is suitable for the PVC, PE plus high-calcium powder ,as well as engineering plastics.
 
The first method of processing screw    Taking the 38CrMoAIA or SACM645 as base material ,and spraying the Ni-20 at the surface of screw arris ,which with the hardness of HRC58-62. The thickness of alloy surface on the screw arris is the standard value of 1.5-3.5mm, which is the alloy of alkaline resistance and corrosion resistance. It is mainly used in the processing of nylon plus 10%-20% fiberglass, PVC, PC ,and high strength engineering plastics.The service life of three or five times longer than the nitrided screw.
 
The second method of processing screw     Taking the SKD61 or SKD11 as base material .Moreover , the material of 30CrMoVg34CrAINi7X35CrMo17X22CrNi17 can also used into processing .
Through the quenching and permeability nitrogen treatment , the hardness of screw can research HRC60°-65° ,which with characteristic of high hard wearing, hard corrosion. It is suitable for processing of XPS, film, blowing machine, PE aluminum-plastic plate, chemical fiber equipment, EPE foaming material , Granulation of waste plastics, PE pipe, WPC, etc.The service life of five or eight times longer than the nitrided screw.
 
Screw speed (rpm)m)
Ø35/Ø77
810
10-70
5-50
Ø45/Ø90
990
50-80
5-45
Ø50/Ø105
1070
100-150
4-45
Ø51/Ø105
1220
100-150
4-45
Ø55/Ø110
1220
120-180
4-40
Ø60/Ø125
1320
150-200
4-40
Ø65/Ø120
1440
200-250
4-40
Ø65/Ø132
1440
200-250
4-40
Ø70/Ø140
1460
220-300
4-40
Ø75/Ø150
1480
250-320
4-35
Ø80/Ø143
1800
300-360
4-35
Ø80/Ø156
1660
300-360
4-35
Ø92/Ø188
2000
400-500
3-35

 

 
 